高温加热条件对合金元素贫化的影响
<TABLE borderColor=#b5dba2 cellSpacing=0 cellPadding=0 width="80%" border=1><TBODY><TR bgColor=#e9fde4><TD width="11%"><DIV align=center>合金牌号</DIV></TD><TD width="18%"><DIV align=center>加热规范
</DIV></TD><TD width="27%"><DIV align=center>加热设备及保护措施
</DIV></TD><TD width="12%"><DIV align=center>贫碳层/mm
</DIV></TD><TD width="15%"><DIV align=center>贫硼层/mm
</DIV></TD><TD width="17%"><DIV align=center>备注
</DIV></TD></TR><TR><TD width="11%"><DIV align=center>GH135
</DIV></TD><TD width="18%"><DIV align=center>1160℃保温4.5h+
1140℃保温4h
</DIV></TD><TD width="27%"><DIV align=center>电炉
</DIV></TD><TD width="12%"><DIV align=center>1
</DIV></TD><TD width="15%"><DIV align=center>3
</DIV></TD><TD width="17%" rowSpan=5><DIV align=center>W、Mo、Al、Ti、Ni、Cr、Mn、Si等合金元素无明显贫化现象
</DIV></TD></TR><TR><TD width="11%" rowSpan=3><DIV align=center>GH37
</DIV></TD><TD width="18%" rowSpan=2><DIV align=center>1200℃保温30min
</DIV></TD><TD width="27%"><DIV align=center>电炉和液化石油气保护
</DIV></TD><TD width="12%"><DIV align=center>0
</DIV></TD><TD width="15%"><DIV align=center>0.8~1.5
</DIV></TD></TR><TR><TD width="27%"><DIV align=center>电炉和玻璃或陶瓷涂料保护
</DIV></TD><TD width="12%"><DIV align=center>0
</DIV></TD><TD width="15%"><DIV align=center>1.6~1.8
</DIV></TD></TR><TR><TD width="18%"><DIV align=center>1190℃保温4h+
1050℃保温4h
</DIV></TD><TD width="27%"><DIV align=center>水煤气无氧化加热炉
</DIV></TD><TD width="12%"><DIV align=center>0
</DIV></TD><TD width="15%"><DIV align=center>4.8
</DIV></TD></TR><TR><TD width="11%"><DIV align=center>GH49
</DIV></TD><TD width="18%"><DIV align=center>1220℃保温4h+
1050℃保温4h
</DIV></TD><TD width="27%"><DIV align=center>水煤气无氧化加热炉
</DIV></TD><TD width="12%"><DIV align=center>0
</DIV></TD><TD width="15%"><DIV align=center>2
</DIV></TD></TR></TBODY></TABLE><P> </P>