低合金钢用实芯焊丝和焊棒对照表

HEATS

, U9 t4 s2 a$ O8 E" g. } C# W5 L1 B* [) ~' ]# h E% x8 y0 }0 j% l) i1 \; Z# g& t1 |, {6 H0 s. E4 P5 A, T- B, I- i. z+ f+ P, p) a& ^) G! Y3 F! c" l% Z; X: x9 U6 n1 z( ?+ R- U7 f+ U, V4 H b9 _4 q" V+ d L8 v S8 @* W6 E G7 n$ @2 @& l- Z( S: i) [5 Z5 r, n6 y! S: c% k; C6 f% {8 y: _2 W* K1 X! A& y# W/ C/ A1 r; @( I: c3 p5 j1 L1 S9 O) L' c3 J( j ? j% [9 H4 Y4 Z# `9 Y3 d2 S+ C8 T' |* a$ x4 K# I! _ p6 [0 x3 s2 L# ~7 s: |* P. \( _8 E9 o R9 ~) b6 z* ]; m$ Y: [& w; l9 q* m- m* `# c4 _ k5 g: T) e& z, X! [; `; B& |* |5 l }. G4 e/ ?$ ?$ c. e9 Z( s) F! A! v' {, p' O: K/ g9 K0 W5 `) F5 q4 m& v* D/ w4 E" U) z! {# A% q) `# l: h0 L" P5 @, m p( ?4 C( ~! B8 i4 e" i5 t8 v: c- U2 P4 o9 S' l2 S1 \. o+ z6 m1 d9 n& v# B% W# A$ y/ y( o: p9 g1 j0 c; U' N% k# q8 x X: S5 G4 d9 I$ s, X- y% g; b" G1 w9 t( a J7 A V+ s9 l$ r8 s" U. |' k- M4 w K7 n5 i/ {5 p% ~. B' r* m' L# m; c& ^- r- Y$ K8 v; g! r y9 e# ~% d8 I. F6 O1 m$ d0 L! I3 N: C( H# q% W/ V" J# c$ D' N+ P# j2 c; h( f& P/ a9 P Y0 l/ y/ V( U+ t" f+ ]) P/ g% ~( k+ `( u: a& n" ^, h- H, N2 ?; d# s3 Q4 k/ |; @% J6 J2 f% ^0 x' v3 J9 ^7 V. \9 ^+ D, e \& r% t% `5 R7 R' }: A8 e7 l, R. s8 a- i3 o# p' }' ~; ]$ m+ @4 d) R8 _$ n% y2 }- a6 p. T9 g( [: `) }. r( g# q, T5 U Y/ e! r, o7 G* {/ _! ]& b) ~6 f% x

中 国	美 国	德 国		瑞 典	瑞 士	荷 兰	日 本
GB	AWS	DIN	THYSSEN	ESAB	UTP	FILARC	JIS	神钢	新日铁
ER55-B2	ER80S-B2	SG CrMo1		OK Autrod 13.12 OK Tigrod 13.12	UTP A 641	PZ 6042 PZ 6542
ER62-B3	ER90S-B3	SG CrMo2		OK Autrod 13.22 OK Tigrod 13.22	UTP A 640	PZ 6043 PZ 6543
ER55-C1	ER80S-Ni1			OK Autrod 13.26
ER55-C2	ER80S-Ni2		Uniox Ni2.5		UTP A 6025	PZ 6040 PZ 6540
ER55-D2	ER80S-D2	SG Mo		OK Autrod 13.09 OK Tigrod 13.09	UTP A642	PZ 6041 PZ 6541	YGW 23		YM-18
	ER80S-G	SG Mo SG CrMo1	Uniox I Mo Uniox I CrMo				YGW 17 YGW 21 YGW 23	MG-60 MGW-50B MGW-50TB MGW-588	YM-53E YM-60C YM-60A YM-60S
	ER100S-G					PZ 6047 PZ 6547 PZ 6048 PZ 6548			YM-70C YM-70A YT-70