日本压铸铝合金机械性能表

HEATS

' V. d' T" s, f5 T w. A8 @& @5 A: w+ F* j. Z' `, ^ [' T2 \, k k6 Y/ @; ]8 b( v4 A4 ~" Y7 R' ^- t9 L% X$ I' J( z0 G4 k: I5 V8 C! S) i0 Z. g6 o4 @6 i c$ v" F" l1 J3 k& f. ]. v4 m$ e8 d2 |" o0 l$ X+ B( d+ l# j" m U9 f! f" Q" o f- Z! J/ F& ]6 C6 O& t6 @, E* t$ F9 r0 t6 E. G& p3 W" k0 t. R2 Y4 v5 h- Q3 m |6 R# u K( w; p; L# A- I. D- L; l% Z1 N& }; Z. j" D* \( C5 D( X* D, f$ B& [' {4 ~6 F! W3 b# p6 j q& h j! H b8 c1 ?5 V3 t2 Z) ^' g- M, n4 D0 C3 ^ \7 V2 a& f7 e1 O( Q( W8 d' ]: ~7 A' D( v0 I% C; H) j6 S0 r' }; ]0 Y2 w. M. N' o) z* ^% o% n( L+ E" ?* M# W# p/ \, ?* [; A3 Q7 V7 r' g/ i4 V. b2 @& m' `2 B5 {% k: T" l o* G: Q- a( M# E" j& l h! z: h0 j# p7 c5 F/ F; H9 r* G; e& M, c g( f2 z+ _9 W+ j K/ l4 X! t% h2 l* a, X Q9 F! h6 `6 `9 Y4 \8 h n( p% p$ Z8 ]3 K& B$ H2 N2 f" }! _; i9 G. E+ H+ ?! G# {' f+ }. x0 C4 l2 p) N6 f) h) S9 P3 D; l0 @9 ?, j% I/ _( {6 Y- q; M, q$ ^2 [, |% g& [3 g) d- X- i" w, u7 | I4 p; f, m0 _& f0 }! B" u4 z( x9 ]" I' S5 o8 `: _1 c2 h* D$ Q; k& r( } {* [, {/ s, B1 T0 @ h2 |! j2 I% z. k& r' \( H3 F7 U/ ~8 Z' A. c' G: ~: t8 C6 X& O. h& d2 j! X( U0 R4 Q0 z9 O n+ e2 ?+ Q0 V2 T8 ]+ q5 q1 d- b' e# Q) I' M6 T C' C0 J; h, q) _; i, ]) Q2 o; m- Q$ ~8 G9 n4 e" Z. X0 [- r: l4 R! C2 `5 b# A# K' E$ N$ v, V. c6 `7 Z9 q8 }$ |4 ^2 R' i" V |9 z" ~5 w7 X! w7 O! C9 @' }7 H0 }1 }# D1 A8 q0 N& K% [. f$ M3 M8 @6 l1 G9 t0 p" m; z6 i7 G& ^" I& A, Z' M' @6 X$ N q; K) N+ m7 m& C

牌号	抗拉试验									硬度试验
	抗拉强度MPa			耐力MPa			延伸率%			HB			HRB
	平均值	σ	ASTM	平均值	σ	ASTM	平均值	σ	ASTM	平均值	σ	ASTM	平均值	σ
ADC1	250	46	290	172	22	130	1.7	0.6	3.5	71.2	3.5	72	36.2	5.5
ADC3	279	48	320	179	35	170	2.7	1.0	3.5	71.4	1.8	76	36.7	2.2
ADC5	(213)	65	310	(145)	26	190			5.0	(66.4)	2.4	74	(30.1)	3.7
ADC6	266	61	280	172	23		64	3.2	10.0	64.7	2.3	67	27.3	3.9
ADC10	241	34	320	157	18	160	1.5	0.5	3.5	73.6	2.4	83	39.4	3.0
ADC12	228	41	310	154	14	150	1.4	0.8	3.5	74.1	1.5	86	40.0	1.8
ADC14	193	28	320	188	31	250	0.5	0.1	<1	76.8	1.7	108	43.1