冷挤压钢的球化退火工艺规范

HEATS

E: `5 D3 [. u7 o* ?8 v6 t ~3 S+ t1 i$ x% I1 S9 r7 ^- ?* @$ Q7 i4 @5 v8 q- U f7 e$ |7 B! N: p( U/ g- k2 f- t: c2 c8 e! ?( I" p) @3 P _0 E* k, T- I- v0 G6 d, I/ g+ Y# S& x, G, T0 b; \: q1 c$ _+ v( [' ~6 D4 M7 i, O' J, ~" |0 n. a% ]2 e# L% v- S( ]* ~( v" U* `: v: ~0 Q7 q3 _# ?. }1 T* a {2 ?$ i# @0 P% ?9 J9 C1 ^9 O% A' U; g( _" d4 ?* K x9 E( x+ a2 w" w. N' o5 U5 m& c/ F0 s! D& L5 s' D- j2 H" m) P) o: h) }* i: [9 E0 P0 ?* D6 B9 d% M' b* L9 o4 @9 K+ e. Q: v/ Z* o! U$ Z7 E2 S: a7 J% e, Y3 }/ _# x; J- v+ }" M0 K+ \+ j1 m1 h! n z7 Q$ d( G7 [8 Q0 Z; M& i, p4 z7 R# `7 {' {+ g+ |, Q+ M" D O0 x7 z/ @1 s7 l5 o( A$ }+ K* H+ U$ h5 q6 F0 [. L% d/ ~/ [3 }# s( `" x7 y) K0 @, j$ \/ J; e. {4 i2 y* F& w5 Q2 W+ d" ^' ?2 i3 ^0 L. ~: p8 G6 U; b* p: q, g8 Z, l$ z; D0 l4 U0 S1 }7 H, K4 b# A4 J( m: P* R. Y- ^1 d9 x0 G) v+ Q. V) ]. ]6 D, J4 N' {2 `' Z: S3 t! E1 A% I, K( d- B8 k8 r8 ~" x( T! M1 S6 k2 |; z3 i" |$ [" N7 _4 Q2 }! I) o. f6 m$ a& H" S! r8 g/ J; }7 j) \ O+ N8 Z7 G3 b" c; t; d. Q: a+ w. Q& j( \0 T0 s8 J, y! a9 t G; p: V7 u$ T0 o+ h c X9 j+ P8 ~2 s; e/ n5 k4 k! Q v& }7 I) B5 f2 K, w% p: |! H9 V p2 {* r, u, V& \7 K6 w

钢 号	退火前硬度（HB）	加热温 度（℃）	保温时间（h）	等温温度及时间（℃-h）	冷却速度（℃/h）	出炉温度（℃）	退火后硬度（HB）
15Cr,20Cr	170	860±10	3～4	-	<50	<130	300
15Cr,20Cr	170	780±10	2～3	700±10-6～8		125～131	500
15Cr,20Cr	170	720	5～6	-	<50	≤125	450
35,45,40MnB	>180	720	6～7	-	<50	≤145	550
08,15,20	150～180	720	2～3	-	空冷	≤120	-
20MnV,40Cr,50	187～217	950～1000	1～1.5	700-2～2.5	60	140	500
40Cr	-	770±10	4～5	670±10-5～6	炉冷	≤160	500

! @5 Q8 g$ j2 f9 q; H& w$ ]