镀锌钢板点焊的焊接工艺参数

HEATS

% d* d% h% d# K7 a2 y9 |9 C$ m8 W. f* D# I8 ?+ m3 O1 ?' p; a- M ^6 q+ o9 x$ C) Z- x& ] M% T+ c! ~5 S7 B" [0 F& c$ e, R: B3 p! j! g0 P( e+ F' l0 N3 B% Q4 `9 J4 x( t- z2 T9 v) _3 C& U6 n. x3 J L5 A* I- I3 D$ N& a( |+ q, F2 ]/ r [ ?9 Z0 m& v& l( t1 M5 F0 V# z6 m3 B5 {; P$ @8 { R4 k- u: p5 W" Y" o; U4 b: W" X# v* ~7 z" n2 w! Y& x& f/ L: V X. u' s+ O* Z$ P, S" }# O3 @- Y$ y/ A& I4 A1 p( |' N' Z! y- _: E1 e. z; G" f; _0 X' V1 p% Y6 o7 t1 n+ E1 ]* K }3 I3 h5 [! l& O* G' T" M% g; D5 `6 F9 ?; Q y$ t( ~3 o: [8 n( `5 N( c8 L- }/ D! Z) y+ W% k3 `' v# j. ?" \- D/ B# D ~; C' Z/ B! W: G& o. I1 S2 j, u9 x% t3 K/ O9 T% t1 q) H I( R; Z* \- }# w0 J3 B* [1 l5 [3 Y- v, w. [, m; E( P% j; ] u5 Q" J+ s8 ^+ X0 i# n# ?. Z2 Y/ e1 f) N# u1 W- \$ g% Y" v2 e% F+ o. X7 H4 b7 `* R. |! w/ x, k5 r7 g0 O( `4 l9 Q: [% D0 h; l/ j: F! {; b1 H( g4 _2 h; z! K+ d2 j* d1 Y4 i0 ^4 c+ X8 _4 U. R) ~' j( b8 M0 H4 h' p9 j9 L2 L* I+ l6 z. W, g/ A1 b2 |5 H. ?8 e' f9 W" c0 J5 L4 u J$ E y* t/ B5 i& ?/ T9 h, |9 I, B# `: O% n/ S% R0 q% A' _; {0 ?" o- p0 B' e$ @8 C" o; P- ~* K/ r5 g! [- i7 M/ H) E' ], w; z* P( j3 {; i7 S1 W2 M# G* b; ?! W c9 C7 u1 R1 \ G6 R: N; ^7 E7 P! ~# X2 J. d5 w6 @" i3 k9 V6 j& E/ e1 t! D' y# Z. \6 r: r* C Q! i' F/ Z( E# V, d: A, m* ?9 u* ]5 v% |+ a: {9 R" O& m }# T6 p$ h+ g5 i8 K S9 x. u: E5 G0 L2 f/ }7 T \: e- {8 r Y% F" o% b: i. n! i6 {2 b7 ~3 H3 {- t# B- }1 c4 z3 w/ m! C3 v4 S3 c" A5 |: F* k) B4 g" \4 J" ]2 O# u- s8 o6 q( y6 n3 |; W C/ A% s0 S' r# l) q8 |4 m* ~4 C+ N$ E& i( y" i9 x0 X7 b( U) X6 g& e" m; k; a; r: |1 C: B8 e4 y) \, U0 `; Y! u& u5 }, U. U! f( n* k7 ]6 v; ^% Z/ d' a) ?5 F" m/ Q% u/ ^6 p% U9 n! B: s! M0 K. I' P, a7 B7 Y: o, ~- x9 \3 n4 m$ J/ @1 I, x7 a8 z7 ^" _# w/ q; W: [* c2 G. y& ?8 s! l/ t) s$ E8 u0 v7 k' K, M: I- B5 B5 w" A7 _1 P! I' K6 Z0 O7 X) L: U. N7 p: X( \; M5 V) U F) q; U8 `( u: I! U! u6 N0 A+ g5 x$ @) f0 J. S4 f; U. x, k/ C8 N ?" z# ^* X8 m/ [* Q/ J5 x0 L6 e6 r3 ^4 ]0 O1 L& w6 C K0 I, X& e7 a, M2 E- E! \6 b( D2 k9 ^- T* \& g5 }! O I; g# ]2 Q5 k! V! F: _4 m& P, E7 T! R# X+ L9 M: c- d4 S h1 J7 j7 }, O0 p b# I$ ^# s0 c! ~7 k. b% Y9 o3 Q2 f: {& R, w9 Z* s. {# {5 K* K/ K( O0 M0 N% i0 S9 p0 E- R# L- N9 q( b. N% q* H+ U1 N5 H, B+ V% ^# F6 L; F9 b$ T& P# G, W. N: n }4 F o. @9 H' R: X" v- i. s9 `% _$ |% u# Q ^8 e, D- D R8 b" C* Z6 {$ ~, j* q# e9 ~3 x. q4 f0 B1 s4 w4 d4 s o' A; w# } E/ _( e' S5 m$ D, e* q: O6 h# O- Y" H% E: R7 ~ \( ?9 J- }# T# q* W S! e! j9 \: j4 j# B( t% E. K) s3 P# q6 W) G: r6 y' i/ V$ [: {& z) m7 I. \" v) W9 R0 ]7 _. ]* l4 ?8 Z; U+ q5 D3 k1 J6 {" h5 R9 n+ ~+ J$ l- A$ b1 O: u; v; A; b R% ]2 ^: r3 H0 D) m9 k* b+ D b9 @& i! {2 Q) q% T# G3 a5 f4 v9 `' Z! p% i: p( k1 ^; X3 J$ Z- R$ F. @5 _% i' i: m, Y, ?& L" Z$ B( V! q' M$ \* {# g5 O- y* M+ ~- O8 N5 E4 `; s- A+ m' J( B6 Z* L5 ^- F% T7 L/ O% |$ d% l0 O8 |5 i7 u; |$ U' i5 t: Y6 l$ ]/ h5 z! `, D6 z+ G+ o7 U1 t3 z( {7 p& ]" E# M: O2 A# f# f4 [% f* M8 ?( ]) n! E0 K2 `7 J/ l$ H4 s$ f& l8 f: U7 l7 |+ z K t% z+ X2 X* k7 @7 B- t* `9 S) l2 x# |8 w5 d% H& h% T. l g, x; M6 N7 P" `! a0 G+ i% ?( k+ p c( W* T1 N4 t+ L+ G1 w4 j5 p8 r) T. s+ P2 | U# F: x5 ]! X" b% G. F8 z l% v7 ^# p- S$ [6 G3 m$ c% |0 m3 @2 O/ |$ U" `0 Y# t+ M/ I6 D4 j: o# u' X& O1 C3 @* w& {' Q# G$ H, p d7 a' v1 O2 c Y+ J- s2 P* h6 @: p7 D1 o, A& T- p/ `* `8 w6 F6 j! h5 ~. I$ P8 H! a( d8 w, M& h$ F* e/ O6 {" r0 ^& s3 _3 {

类    型	板    厚 (mm)	镀层厚度 (μm)	A    级			B    级
			焊接电流 (A)	电极压力 (N)	焊接通电时间 (周波数)	焊接电流 (A)	电极压力 (N)	焊接通电时间 (周波数)
熔化法镀锌钢板	0.4	10～15	7900	1200	6	6500	1000	8
	0.5	10～15	8800	1450	7	7300	1250	10
	0.6	10～15	9700	1750	8	8000	1500	12
	0.8	10～15	11200	2350	11	9200	2000	16
	1.0	15～20	12500	3000	14	10300	2500	20
	1.2	15～20	13700	3550	17	11300	3000	24
	1.6	15～20	15800	4700	22	13000	4000	32
	2.0	20～25	17700	5900	28	14600	5000	40
	2.3	20～25	19000	6700	32	15600	5800	46
	2.8	20～25	20900	8000	40	17200	7000	56
电镀锌钢板	0.4	2～3	7400	1200	6	6000	850	8
	0.5	2～3	8300	1500	7	6700	1100	10
	0.6	2～3	9100	1800	8	7400	1350	12
	0.8	2～3	10500	2700	11	8500	1800	16
	1.0	2～3	11700	3100	14	9500	2300	20
	1.2	2～3	12800	3700	17	10400	2600	24
	1.6	2～3	14800	4800	22	12000	3700	32
	2.0	2～3	16500	6000	28	13400	4600	40
	2.3	2～3	17700	7000	32	14400	5300	46
	2.8	2～3	19600	8400	40	15900	6300	56
合金化处理的熔化法镀锌钢板	0.4	8～12	6700	1150	6	5700	800	8
	0.5	8～12	7500	1450	7	6400	1050	10
	0.6	8～12	8200	1750	8	7000	1300	12
	0.8	8～12	9500	2300	11	8100	1700	16
	1.0	8～12	10600	3000	14	9000	2200	20
	1.2	8～12	11600	3600	17	9900	2700	24
	1.6	8～12	13400	4700	22	11400	3600	32
	2.0	8～12	15000	5900	28	12700	4500	40
	2.3	8～12	16100	6800	32	13600	5100	46
	2.8	8～12	17700	8600	40	15100	6200	56

; W6 C! x8 s8 h/ T+ g- `

注:	焊接电源为交流,60Hz。