浇注时碳钢低合金钢件工艺出品率

HEATS

5 Y" Q- E* q/ V0 U" n) P ?% h7 H; ?3 a: \& i5 O4 }0 H4 Y- {1 c$ r- X# t0 X* |; ]9 a9 G/ q7 W3 ]6 e" U& z! w% q. X. k: x% p& y. @0 K8 m6 f7 v0 `# c: t4 l1 ?: p+ m9 v) F" z7 k2 c9 I9 r: f% t/ B$ m- v% t8 L/ ]: _9 F' n0 j9 V; D* {7 O' i" C- U: q, |# v+ B. {# S# d2 u7 C4 S0 e7 g! M; m2 ]* E4 t8 }% l! J( U" n5 k" B' A9 ?" {+ ?& s# ]4 ]' x; e& @6 I! `: K4 `+ V/ ]- K, d3 J' m) W; q$ q" c/ k# @6 [/ W6 u6 \3 w& w" F# z; y6 X# N4 W: d) q8 S+ T. t9 w0 J, [ I" e E- j- p( j: g h: {3 X5 \ w* g4 H$ U: w) b, }* _2 N+ x6 Q: |4 v0 ]0 ^4 z2 l' x5 A( h3 X8 j1 G3 _1 @* f' v. j7 R6 X$ R+ x1 |, W( P" ?3 g6 C8 u B* l) `9 E/ _& w* A6 o5 f) [4 P" t& p W2 J3 G+ }+ b- v3 O, F# g% J& s$ A& a2 d+ O0 s# L8 O* C' _% j$ d& w* R, G+ M1 G1 c8 z; e% }- t% N+ e& {& i2 }: S+ k+ B) c) ^& `) Q7 L! U' O) K+ o8 e3 ]" o: c ~0 M! o) J& l& U& O! q& h) I1 i) x7 l2 h) x+ g$ m4 N8 I: e6 K# o9 f" v1 n) H. j( x. Q3 _/ r1 |3 t6 R& D; L5 [+ h, H- T; s2 p( V2 Q# @9 z7 `# o+ k$ n/ w( ?0 _8 X& I- |* S- |& e6 v3 Z3 J! s) O' e( {. j. a) O# R0 x( | A3 z& ?, q: N8 i) O5 k/ j& Q ~" H) `* Q$ O6 ~ ^; s" z8 E8 G3 ^$ h! I) W7 n9 K9 X# k9 i7 y- @) B0 _( d1 x3 T/ _8 z# A: L# Y# J P0 E6 w0 ]' f) _* z+ l! [3 B

铸件重量下限	铸件重量上限	主要壁厚下限	主要壁厚上限	加工面比例下限	加工面比例上限	明冒口工艺出品率	暗冒口工艺出品率
0	100	0	20	50	100	58-62	65-69
0	100	21	50	50	100	54-58	61-65
0	100	50	100	50	100	51-55	58-62
0	100	0	20	0	50	63~67	68~72
0	100	21	50	0	50	59~63	65~69
0	100	50	100	0	50	50~60	62~66
101	500	0	30	50	100	63~67	68~72
101	500	31	60	50	100	61~65	64~68
101	500	60	100	50	100	58~62	62~66
101	500	0	30	0	50	65~69	68~72